ELCRES™ EXL1213T Resin Transparent Clear, Better Chemical Resistance

Non Reinforced with Improved Low Temperature Impact Strength

ELCRES™ EXL1213T Polycarbonate Copolymer Resin is a Transparent, Non‑Reinforced Engineering Thermoplastic developed for applications that require Visual Clarity combined with Toughness at reduced Temperatures. This Clear Polycarbonate Copolymer is designed to maintain Ductility at Temperatures Down to ‑30 °C, supporting reliable performance in Environments where both Aesthetics and Low‑Temperature Impact Resistance are Important.

Optical and Surface Characteristics of ELCRES™ EXL1213T Polycarbonate Copolymer Resin enable the production of Clear Components with consistent Appearance and Refined Surface Quality. The Transparent Nature of the material support applications where Visibility, Light Transmission, or Aesthetic integration are Key Design Considerations.

Low‑Temperature Mechanical Performance is enhanced through the improved Impact Resistance and Ductility of ELCRES™ EXL1213T Polycarbonate Copolymer Resin, reducing the Risk of Brittle failure under Cold Condition Loading. This Performance profile makes the material suitable for Parts Exposed to Cooler Operating Environments without Sacrificing Clarity.

Processing advantages of ELCRES™ EXL1213T Polycarbonate Copolymer Resin are defined by its superior Flow Behaviour, enabling Efficient Mold Filling and Shorter Cycle Times. This Flow Profile support Ease of Processing and Improved Productivity while maintaining Consistent Part Quality across Complex Geometries.

Chemical Exposure Resistance is improved through the formulation of ELCRES™ EXL1213T Polycarbonate Copolymer Resin, supporting use in applications where contact with Chemicals or Cleaning Agents may Occur. This Enhanced Resistance contributes to Extended Part Life and Surface Stability over Time.

Regulatory Classification of ELCRES™ EXL1213T Polycarbonate Copolymer Resin is defined by its UL Rating. ELCRES™ EXL1213T is UL94‑HB Rated at 0.70 mm ~ 3.0 mm, indicating suitability for applications requiring baseline Flame Performance without Flame‑Retardant Additives. Environmental alignment is supported by its ROHS Compliant Status, enabling Use in Global Markets.

Notes :

ELCRES™ EXL1213T Polycarbonate Copolymer Resin
Low Temperature Ductility
Transparent Colored
UL94 Rated
ROHS Compliant

ELCRES™ EXL1213T is a Transparent Clear ROHS Compliance Polycarbonate Resin

Vicat Softening Temperature Rate

Vicat Softening Temperature rate , B50 = 140

Material MFI / Melt Flow Rate

Melt Flow Rate, 300°C/1.2 kgf = 14.7

Material Melt Volume Rate, MVR

Melt Volume Rate, 300°C/1.2 kg = 13.3

Material Flexural Modulus

Flexural Modulus, ISO 178, 2 mm/min, MPa = 1950

ELCRES™ EXL1213T Resin are UL94 - HB@0.70 mm ~ 3.0 mm

ELCRES Main Page

Disclaimer

Any sale by SABIC, Its Subsidiaries and Affiliates (each a “Seller”), is Made Exclusively under Seller’s Standard Conditions of Sale (available upon request) unless Agreed Otherwise in Writing and Signed on behalf of the Seller. While the Information Contained herein is given in Good Faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Customer must Determine the Suitability of Seller Materials for the Customer’s Particular Use through Appropriate Testing and Analysis. No Statement by Seller Concerning a Possible Use of any Product, Service or Design is Intended, or should be Construed, to grant any License under any Patent or other Intellectual Property Right. © 2021

SABIC Innovative Plastics is a Trademark of SABIC Holding Europe BV * Cycolac, Cycoloy, Elcrin, Elcres, Lexan, Noryl, Ultem, Xenoy, Valox and Visualfx are Trademarks of SABIC Innovative Plastics IP BV © Copyright 2008 SABIC Innovative Plastics IP BV. All rights reserved.