ELCRES™ ML0111 Resin Opaque Color High Flow. For IMT or IML Process

Advanced Polycarbonate Siloxane Copolymer with High Impact Resistance

ELCRES™ ML0111 Polycarbonate Siloxane Copolymer Resin is a High Flow Engineering Thermoplastic specifically developed for advanced In‑Mold Processing Technologies. This Opaque, Non‑Reinforced material is optimized to support In‑Mold Thermoforming and In‑Mold Labeling applications where Flow, Surface Conformity, and Mechanical Toughness are Critical.

Processing Performance is a defining attribute of LNP™ ELCRES™ ML0111 Polycarbonate Siloxane Copolymer Resin, with a High Flow Profile that enables Smooth Resin Distribution over Complex Mold Surfaces. The Unique Flow behaviour support uniform Coverage and Accurate replication during IMT and IML Processes, reducing Forming Stress and Enhancing Process Reliability.

Mechanical behaviour of ELCRES™ ML0111 Polycarbonate Siloxane Copolymer Resin emphasizes High Impact Resistance, allowing Finished Components to maintain Durability after Forming and Decoration. The Toughened Siloxane‑Modified Polymer Structure helps resist Cracking and Damage during Post‑Forming Handling and End‑Use.

Surface and Aesthetic Stability are supported by the balanced material Response of LNP™ ELCRES™ ML0111 Polycarbonate Siloxane Copolymer Resin, enabling consistent appearance and structural integrity in Decorated Parts. This Stability is particularly important in applications where the Final Surface is directly integrated into the Molded Component.

Processing Efficiency benefits are further enhanced by the Ease of Molding Associated with ELCRES™ ML0111 Polycarbonate Siloxane Copolymer Resin, supporting reliable Cycle Control and reduced Processing Complexity. This makes the material well suited for High throughput manufacturing Environments Utilizing In‑Mold Decoration Technologies.

ELCRES™ ML0111 is UL94‑HB Rated, 0.40 mm ~ 3.0 mm, supporting use in applications where baseline flammability requirements apply without the need for Flame‑Retardant Formulation. Environmental alignment is supported by its RoHS Compliant Status, enabling Global Application.

Notes :

ELCRES™ EXL1213T Polycarbonate Copolymer Resin
Glass Fiber Reinforced Rail Applications
Opaque Colored
High Flow
RoHS Compliant

ELCRES™ ML0111 is a Opaque Color RoHS Compliance Polycarbonate Resin

Vicat Softening Temperature Rate

Vicat Softening Temperature rate , B50 = 117

Material MFI / Melt Flow Rate

Melt Flow Rate, 300°C/1.2 kgf = 20

Material Melt Volume Rate, MVR

N/A

Material Flexural Modulus

Flexural Modulus, ISO 178, 2 mm/min, MPa = 2300

ELCRES™ ML0111 Resin are UL94 - HB@0.40 mm ~ 3.0 mm

ELCRES Main Page

Disclaimer

Any sale by SABIC, Its Subsidiaries and Affiliates (each a “Seller”), is Made Exclusively under Seller’s Standard Conditions of Sale (available upon request) unless Agreed Otherwise in Writing and Signed on behalf of the Seller. While the Information Contained herein is given in Good Faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Customer must Determine the Suitability of Seller Materials for the Customer’s Particular Use through Appropriate Testing and Analysis. No Statement by Seller Concerning a Possible Use of any Product, Service or Design is Intended, or should be Construed, to grant any License under any Patent or other Intellectual Property Right. © 2021

SABIC Innovative Plastics is a Trademark of SABIC Holding Europe BV * Cycolac, Cycoloy, Elcrin, Elcres, Lexan, Noryl, Ultem, Xenoy, Valox and Visualfx are Trademarks of SABIC Innovative Plastics IP BV © Copyright 2008 SABIC Innovative Plastics IP BV. All rights reserved.