LEXAN™ EXL1414H Copolymer Opaque Resin, Low Temperature Ductility
Hydrolytic Stability. Unique Low Temperature -40°Celsius Ductility
LEXAN™ EXL1414H Polycarbonate Resin is an Opaque Polycarbonate Copolymer material engineered for applications requiring Low Temperature Ductility, Hydrolytic Stability, and Chemical Resistance. This Grade is designed to maintain performance in Environments where both Cold Conditions and Moisture exposure are Present, making it suitable for demanding Industrial and Automotive applications.
In Environments where Materials are exposed to Cold Temperatures combined with Humidity or Water Contact, maintaining consistent Mechanical properties is Critical. This Grade is formulated to deliver reliable Impact performance at -40°C, allowing components to Resist Cracking while preserving Structural Integrity under Low Temperature Stress.
A Key Advantage of LEXAN™ EXL1414H Polycarbonate Resin is its enhanced Hydrolytic Stability, which helps Prevent degradation when exposed to Moisture over time. This ensures Long-Term material reliability and Property Retention, particularly in applications where Environmental exposure cannot be avoided.
With its Medium Flow Characteristics, the Resin provides controlled Mold Filling Behavior, supporting accurate Part Geometry and Dimensional Stability. This makes it well suited for applications where Precision and Repeatability are Essential.
In addition to Moisture Resistance, the material offers improved Chemical Resistance, enabling it to withstand exposure to Cleaning Agents and Industrial Environments. This combination of properties supports Durability in Real-World Operating Conditions.
The Siloxane-Modified Structure enhances Impact Strength and Flexibility, allowing Parts to perform reliably under repeated Stress and varying Environmental Conditions. This makes it particularly valuable in applications requiring Durability across Temperature and Moisture Variations.
From a Processing Standpoint, the material supports efficient Molding with stable Shrinkage Behavior. This contributes to improved Manufacturing Consistency and reliable Part Quality, especially in applications requiring consistent performance across Production Runs.
LEXAN™ EXL1414H Polycarbonate Resin is classified as Non UL Rated, making it suitable for applications where Flame Retardancy is not required but Environmental Durability is Critical. In addition, it is RoHS Compliant, aligning with Global Environmental Standards.
In practical use, this Grade is well suited for Automotive Components, Electrical Housings, Outdoor Equipment, and Industrial Parts where Resistance to both Cold Temperatures and Moisture exposure is Essential. Its balanced Property Profile makes it a Dependable Choice for Harsh Operating Environments.
At its Core, LEXAN™ EXL1414H Polycarbonate Resin delivers a Strong combination of Low Temperature Toughness, Hydrolytic Stability, and Chemical Resistance. It provides a reliable Solution for applications requiring Durability, Environmental Resistance, and consistent Mechanical performance in Challenging Conditions.
Notes :
LEXAN™ EXL1414H Polycarbonate Resin
Opaque Copolymer PC
Medium Flow Grade
Low Temperature Impact Strength (to 40°C)
Hydrolytic Stability & Low Moisture Sensitivity
Good Chemical Resistance
ROHS Compliant
LEXAN™ EXL1414H is a Opaque Color ROHS Compliance Polycarbonate Resin
LEXAN™ EXL1414H Resin HDT, 1.82 MPa, ASTM A648, 3.2 mm, unannealed is at 124°C
Vicat Softening Temperature of LEXAN™ Polycarbonate EXL1414H Resin
Vicat Softening Temperature Rate, B50 = 145
Material MFI / Melt Flow Rate
Melt Flow Rate, 300°C/1.2 kgf = 10
Material Melt Volume Rate, MVR
Melt Volume Rate, 300°C/1.2 kg = 9
Material Flexural Modulus
Flexural Modulus, ISO 178, 2.0 mm/min, MPa = 2250
LEXAN™ EXL1414H Copolymer Resin has 0.40 ~ 0.80 Shrinkage, Flow, 3.2 mm. %
LEXAN™ EXL1414H Polycarbonate Resin are Non UL94 Rated
Disclaimer
Any sale by SABIC, Its Subsidiaries and Affiliates (each a “Seller”), is Made Exclusively under Seller’s Standard Conditions of Sale (available upon request) unless Agreed Otherwise in Writing and Signed on behalf of the Seller. While the Information Contained herein is given in Good Faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Customer must Determine the Suitability of Seller Materials for the Customer’s Particular Use through Appropriate Testing and Analysis. No Statement by Seller Concerning a Possible Use of any Product, Service or Design is Intended, or should be Construed, to grant any License under any Patent or other Intellectual Property Right. © 2021