LEXAN™ EXL8414 Polycarbonate Copolymer. 25% Post Consumer Recycled
Low Temperature -40° Celsius Ductility. Low Flow and Opaque Color
LEXAN™ EXL8414 Polycarbonate Resin is a Polycarbonate Siloxane Copolymer formulated with 25% Post-Consumer Recycled (PCR) content using Certified Mechanical Recycling. This Opaque Engineering Resin is designed to balance Sustainability, Low-Temperature Toughness, and controlled Processing Behavior, making it suitable for applications where Environmental Targets must be achieved without Compromising Dimensional Precision or Mechanical Reliability.
For manufacturers Focused on Sustainable Product Development, LEXAN™ EXL8414 Polycarbonate Resin enables Meaningful integration of Recycled content while maintaining consistent Mechanical Performance. This supports Circular Economy Initiatives and Sustainability Targets while preserving Dependable Functionality in Molded Components.
A Key performance Characteristic of LEXAN™ EXL8414 Polycarbonate Resin is its Impact Resistance at -40°C, allowing Parts to retain Toughness and Resist Brittle Fracture in Cold Environments. This ensures reliable performance in Outdoor, Industrial, and Cold-Climate applications where Mechanical Durability is Essential.
Processing Control is a Defining Advantage of LEXAN™ EXL8414 Polycarbonate Resin. Its Low Flow Profile provides improved Control during Injection Molding, supporting Better Dimensional Accuracy, reduced Variability, and stable Replication of Part Geometry across Production Runs. This makes it well suited for Precision components requiring consistent Tolerances.
The Siloxane-Modified Copolymer Structure enhances flexibility and Impact Resistance, allowing Molded Parts to withstand Mechanical Stress, Vibration, and Environmental Fluctuations while maintaining Long-Term Structural Stability.
To support application-Specific Requirements, LEXAN™ EXL8414 Polycarbonate Resin is Supplied in Opaque Formulations with Limited Color Options, ensuring consistent appearance and controlled material Standardization in Sustainability-Driven Product Designs.
From a Manufacturing Standpoint, the material Exhibits stable Processing behavior with Predictable Shrinkage Characteristics. This contributes to Repeatable Production Quality, Dimensional Consistency, and efficient High-Volume Molding Performance.
The Resin Achieves a UL94 HB Flame Rating from 0.75 mm to 3.00 mm, providing Adequate Basic Flame performance for General-Purpose Electrical and Industrial applications. It is also RoHS Compliant, aligning with Global Environmental and Regulatory Requirements.
Typical applications for LEXAN™ EXL8414 Polycarbonate Resin include Automotive Components, Industrial Housings, Consumer Products, and Outdoor Equipment where Recycled Content, Low-Temperature Durability, and Dimensional Control are Key Design Requirements.
Overall, LEXAN™ EXL8414 Polycarbonate Resin delivers a balanced combination of PCR Integration, -40°C Toughness, and controlled Processing Performance, providing manufacturers with a reliable material Solution for Sustainable Yet Precision-Driven Engineering applications.
Notes :
LEXAN™ EXL8414 Polycarbonate Resin
25% Post Consumer Recycled (PCR) Content
Siloxane Copolymer PC
Low Flow Grade (High Precision Molding)
Low Temperature Impact Strength (to ‑40°C)
Good Dimensional Stability
High Toughness & Flexibility
UL94 HB Rated (0.75–3.0 mm)
ROHS Compliant
LEXAN™ EXL8414 is a Opaque Color ROHS Compliance Polycarbonate Resin
LEXAN™ EXL8414 Resin HDT, 1.82 MPa, ASTM A648, 3.2 mm, unannealed is at 126°C
Vicat Softening Temperature of LEXAN™ Polycarbonate EXL8414 Resin
Vicat Softening Temperature Rate, B50 = 143
Material MFI / Melt Flow Rate
Melt Flow Rate, 300°C/1.2 kgf = 9.2
Material Melt Volume Rate, MVR
Melt Volume Rate, 300°C/1.2 kg = 8
Material Flexural Modulus
Flexural Modulus, ISO 178, 2.0 mm/min, MPa = 2170
LEXAN™ EXL8414 Copolymer Resin has 0.40 ~ 0.80 Shrinkage, Flow, 3.2 mm. %
LEXAN™ EXL8414 Polycarbonate Resin are UL94 - HB@ 0.75 mm ~ 3.00 mm
Disclaimer
Any sale by SABIC, Its Subsidiaries and Affiliates (each a “Seller”), is Made Exclusively under Seller’s Standard Conditions of Sale (available upon request) unless Agreed Otherwise in Writing and Signed on behalf of the Seller. While the Information Contained herein is given in Good Faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Customer must Determine the Suitability of Seller Materials for the Customer’s Particular Use through Appropriate Testing and Analysis. No Statement by Seller Concerning a Possible Use of any Product, Service or Design is Intended, or should be Construed, to grant any License under any Patent or other Intellectual Property Right. © 2021