STAT-KON 9X08403C Compound. Liquid Crystal Polymer with Carbon Fiber

Clean Compounding Technology, Flame Retardant, High Heat Resistance

LNP™ STAT-KON™ 9X08403C Compound is a LCP with Carbon Fiber Reinforced and offers Good Barrier Against Water and Oxygen

The Compound Surface Resistivity = 1.E+05-1.E+09 Ω.

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ 9X08403C Featured such as : -
- Electrically Conductive
- Dimensional Stability
- High Stiffness
- High Strength
- Super Strong (Carbon Fiber Reinforced)
- Flame Retardant
- High Heat Resistance
- Low Ionics
- Low Outgassing

Applications Examples

- Electronic Components
- Semi-Conductor
- Computer Tablets
- Electrical
- Semi-Conductor Handling
- Hard Drive Components

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ 9X08403C Resin has a Flexural Modulus of 14400 MPa. 1.3 mm/min ISO 178

STAT-KON™ 9X08403C Resin offers a Tensile Strain, Break, 5 mm/min of - %. ISO 527

SABIC LNP™ STAT-KON™ 9X08403C compound offer HDT, 1.82 MPa of 280°C

LNP™ STAT-KON™ 9X08403C Compound Resin has 0.2% Shrinkage, Along Flow

STAT-KON® 9X08403C Compound are Non UL94 Listed