STAT-KON EJ000C Compound. Polyetherimide Resin Carbon Nanotube

Clean Compounding Technology, High Stiffness & Temperature Resistance

LNP™ STAT-KON™ EJ000C Compound is a Polyetherimide Resin with CNT Reinforced

The Compound Surface Resistivity = 1E+04 – 1E+07 Ω.

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ EJ000C Featured such as : -
- Electrically Conductive
- Carbon Nanotube Technology
- High Stiffness
- High Strength
- High Heat Resistance
- Low Ionics
- Low Outgassing
- Clean Compounding Technology Produced

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ EJ000C Resin has a Flexural Modulus of 3620 MPa. 2 mm/min ISO 178

STAT-KON™ EJ000C Resin offers a Tensile Strain, Break, 5 mm/min of 4%. ISO 527

SABIC LNP™ STAT-KON™ EJ000C compound offer HDT, 1.82 MPa of 201°C

LNP™ STAT-KON™ EJ000C Compound Resin has 0.5 ~ 0.7% Shrinkage, Along Flow

STAT-KON® EJ000C Compound are Non UL94 Listed