STAT-KON EX02598C Compound. Polyetherimide Resin Carbon Nanotube

Clean Compounding Technology, High Stiffness & Temperature Resistance

LNP™ STAT-KON™ EX02598C Compound is a Polyetherimide Resin with CNT Reinforced with Clean Compounding Technology Produced

The Compound Surface Resistivity = 1.E+03 – 1.E+06 Ω.

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ EX02598C Featured such as : -
- Electrically Conductive
- Carbon Nanotube Technology
- High Stiffness
- High Strength
- High Heat Resistance
- Low Ionics
- Low Outgassing

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ EX02598C Resin has a Flexural Modulus of 3110 MPa. 2 mm/min ISO 178

STAT-KON™ EX02598C Resin offers a Tensile Strain, Break, 5 mm/min of 2.1%. ISO 527

SABIC LNP™ STAT-KON™ EX02598C compound offer HDT, 1.82 MPa of 163°C

LNP™ STAT-KON™ EX02598C Compound Resin has 0.6 ~ 0.8% Shrinkage, Along Flow

STAT-KON® EX02598C Compound are Non UL94 Listed