STAT-KON EX11318C Compound. Polyetherimide Resin 30% Carbon Fiber

Clean Compounding Technology, Low C18-C40 Hydrocarbons & Good Flow

LNP™ STAT-KON™ EX11318C Compound is a Polyetherimide Resin with 30% Carbon Fiber Reinforced with Clean Compounding Technology Produced

The Compound Surface Resistivity = 5.E+03-5.E+05 Ω. Low C18 ~ C40 Hydrocarbons and UL94 Rated

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ EX11318C Featured such as : -
- Electrically Conductive
- High Flow
- High Stiffness
- High Strength
- Super Strong (Carbon Fiber Reinforced)
- High Modulus
- High Heat Resistance
- Low Ionics
- Low Outgassing
- Dimensional Stability

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ EX11318C Resin has a Flexural Modulus of 18140 MPa. ASTM D790

STAT-KON™ EX11318C Resin offers a Tensile Strain, Break, 5 mm/min of 1.9%. ASTM D638

SABIC LNP™ STAT-KON™ EX11318C compound offer HDT, 1.82 MPa of 203°C

LNP™ STAT-KON™ EX11318C Compound Resin has 0.1 ~ 0.2% Shrinkage, Along Flow

STAT-KON® EX11318C Compound are UL94 - V0 @ 0.4 mm ~ 0.44 mm