STAT-KON EX12310C Compound. Polyetherimide Resin 10% Carbon Fiber

Clean Compounding Technology, Low C18-C40 Hydrocarbons & Good Flow

LNP™ STAT-KON™ EX12310C Compound is a Polyetherimide Resin with 10% Carbon Fiber Reinforced with Clean Compounding Technology Produced

The Compound Surface Resistivity = 3.97 +05 Ω. Low C18 ~ C40 Hydrocarbons and UL94 Rated

The Compounding is made from Clean Compounding Technology. Feature Low level of Volatiles and Ionics Contamination from Nitrates, Chlorides and Sulfates. It Reduces the Potential of Wafer Damages while promoting more Accurate and Reliable Data Reading

STAT-KON™ EX12310C Featured such as : -
- Electrically Conductive
- High Flow
- High Stiffness
- High Strength
- Super Strong (Carbon Fiber Reinforced)
- High Modulus
- High Heat Resistance
- Low Ionics
- Low Outgassing
- Dimensional Stability

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ EX12310C Resin has a Flexural Modulus of 8410 MPa. 2 mm/min ISO 178

STAT-KON™ EX12310C Resin offers a Tensile Strain, Break, 5 mm/min of 2.3%. ISO 527

SABIC LNP™ STAT-KON™ EX12310C compound offer HDT, 1.82 MPa of 197°C

LNP™ STAT-KON™ EX12310C Compound Resin has 0.5 ~ 0.7 % Shrinkage, Along Flow

STAT-KON® EX12310C Compound are UL94 - V0 @ 0.4 mm ~ 1.3 mm