STAT-KON OE004A Compound. Polyphenylene Sulfide 20% Carbon Fiber

High Temperature Resistance, Chemical Resistance, & High Rigidity

LNP™ STAT-KON™ OE004A Compound is a Polyphenylene Sulfide with 20% Carbon Fiber Reinforced.

The Compound Surface Resistivity = 1.E+01 - 1.E+04 Ω. UL94 Rated

The PPS Compound offers Balance of Properties, such as High Temperature Resistance, Chemical Resistance, Flowability, Dimensional Stability and Electrical Characteristics

STAT-KON™ PPS OE004A Featured such as : -
- Electrically Conductive
- Self-Extinguishing without adding Flame Retardants.
- Good Chemical Resistance
- Good Heat Resistance
- Good Rigidity
- Low Moisture Absorption
- Very Good Thermal Stability

Applications Examples

- Electronic Components
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ OE004A Resin has a Flexural Modulus of 15700 MPa. 2 mm/min ISO 178

STAT-KON™ OE004A Resin offers a Tensile Strain, Break, 5 mm/min of 1.1%. ISO 527

SABIC LNP™ STAT-KON™ OE004A compound offer HDT, 1.82 MPa Flat 64 mm of 256°C

LNP™ STAT-KON™ OE004A Compound Resin has 0.1 ~ 0.3% Shrinkage, Along Flow

STAT-KON® OE004A Compound are UL94 - V0 @ 1.50 mm