STAT-KON OE006C1 Compound. Polyphenylene Sulfide with 30% Carbon Fiber

High Rigidity, High Temperature Resistance and Chemical Resistance

LNP™ STAT-KON™ OE006C1 Compound is a Polyphenylene Sulfide with 30% Carbon Fiber Reinforced. High Rigidity

The Compound Surface Resistivity = 1.E+02 - 1.E+05 Ω. Non UL94 Rated

The PPS Compound offers Balance of Properties, such as High Temperature Resistance, Chemical Resistance, Flowability, Dimensional Stability and Electrical Characteristics

STAT-KON™ PPS OE006C1 Featured such as : -
- Electrically Conductive
- Self-Extinguishing without adding Flame Retardants.
- Good Chemical Resistance
- Good Heat Resistance
- High Rigidity
- Low Moisture Absorption
- Very Good Thermal Stability

Applications Examples

- Electronic Components
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ OE006C1 Resin has a Flexural Modulus of 19640 MPa. 2 mm/min ISO 178

STAT-KON™ OE006C1 Resin offers a Tensile Strain, Break, 5 mm/min of 1%. ISO 527

SABIC LNP™ STAT-KON™ OE006C1 compound offer HDT, 1.82 MPa of 264°C

LNP™ STAT-KON™ OE006C1 Compound Resin has 0.08 ~ 0.1% Shrinkage, Along Flow

STAT-KON® OE006C1 Compound are Non UL94 Listed