STAT-KON RE0039 Compound. Nylon 6/6 based Resin 15% Carbon Fiber

Polyamide 6/6 (PA6/6) Based. Flame Retardant & Electrically Conductive

LNP™ STAT-KON™ RE0039 Compound is a Nylon 6/10 with 15% Carbon Fiber Reinforced. Electrically Conductive with Flame Retardant and High Stiffness

The Compound Surface Resistivity = 1.E+02 - 1.E+06 Ω. UL94 Rated

The Polyamide 6/6 (PA6/6) Compound offers Chemical Resistance to Hydrocarbons & Good Impact

STAT-KON™ RE0039 Nylon 6/6 Featured such as : -
- Electrically Conductive
- Excellent Strength
- High Heat Tolerance
- Good Abrasion and Wear Resistance
- Chemical Resistance to Hydrocarbons
- High Stiffness
- Wear Resistance and Lubricity

Applications Examples

- Electronic Components
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ RE0039 Resin has a Flexural Modulus of 14200 MPa. 2 mm/min ISO 178

STAT-KON™ RE0039 Resin offers a Tensile Strain, Break, 5 mm/min of 2.2%. ISO 527

SABIC LNP™ STAT-KON™ RE0039 compound offer HDT, 1.82 MPa of 247°C

LNP™ STAT-KON™ RE0039 Compound Resin has 0.2 ~ 0.3% Shrinkage, Along Flow

STAT-KON® RE0039 Compound are UL94 - V0 @ 1.5 mm