STAT-KON RE006 Compound. Nylon 6/6 Based Resin with 30% Carbon Fiber

Good Impact & Electrically Conductive Polyamide 6/6 (PA6/6) Based

LNP™ STAT-KON™ RE006 Compound is a Nylon 6/10 with 30% Carbon Fiber Reinforced. Electrically Conductive with Good Impact Strength and High Stiffness

The Compound Surface Resistivity = 1.E+02 - 1.E+05 Ω. Non UL Rated

The Polyamide 6/6 (PA6/6) Compound offers Chemical Resistance to Hydrocarbons & Good Impact

STAT-KON™ RE006 Nylon 6/6 Featured such as : -
- Electrically Conductive
- Excellent Strength
- High Heat Tolerance
- Good Abrasion and Wear Resistance
- Chemical Resistance to Hydrocarbons
- High Stiffness
- Wear Resistance and Lubricity

Applications Examples

- Electronic Components
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ RE006 Resin has a Flexural Modulus of 16950 MPa. 2 mm/min ISO 178

STAT-KON™ RE006 Resin offers a Tensile Strain, Break, 5 mm/min of 2.3%. ISO 527

SABIC LNP™ STAT-KON™ RE006 compound offer HDT, 1.82 MPa of 254°C

LNP™ STAT-KON™ RE006 Compound Resin has 0.1 ~ 0.3% Shrinkage, Along Flow

STAT-KON® RE006 Compound are Non UL94 Listed