STAT-KON RE0069S Compound. Nylon 6/6 Based Resin with 30% Carbon Fiber

Polyamide 6/6 (PA6/6) Based. Flame Retardant & Electrically Conductive

LNP™ STAT-KON™ RE0069S Compound is a Nylon 6/10 with 30% Carbon Fiber Reinforced. Electrically Conductive with Flame Retardant and High Stiffness

The Compound Surface Resistivity = 1.E+01 - 1.E+04 Ω. UL94 Rated

The Polyamide 6/6 (PA6/6) Compound offers Chemical Resistance to Hydrocarbons & added Heat Stabilizer

STAT-KON™ RE0069S Nylon 6/6 Featured such as : -
- Electrically Conductive
- Excellent Strength
- High Heat Tolerance
- Good Abrasion and Wear Resistance
- Chemical Resistance to Hydrocarbons
- High Stiffness
- Wear Resistance and Lubricity

Applications Examples

- Electronic Components
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ RE0069S Resin has a Flexural Modulus of 19560 MPa. 2 mm/min ISO 178

STAT-KON™ RE0069S Resin offers a Tensile Strain, Break, 5 mm/min of 1.4%. ISO 527

SABIC LNP™ STAT-KON™ RE0069S compound offer HDT, 1.82 MPa of 242°C

LNP™ STAT-KON™ RE0069S Compound Resin has 0.1 ~ 0.3% Shrinkage, Along Flow

STAT-KON® RE0069S Compound are UL94 - V0 @ 1.5 mm