STAT-KON RE008 Compound. Nylon 6/6 Based Resin with 40% Carbon Fiber

Good Strength & Electrically Conductive Polyamide 6/6 (PA6/6) Based

LNP™ STAT-KON™ RE008 Compound is a Nylon 6/10 with 40% Carbon Fiber Reinforced. Electrically Conductive with High Impact Strength and High Stiffness

The Compound Surface Resistivity = 1.E+01 - 1.E+04 Ω. UL94 Rated

The Polyamide 6/6 (PA6/6) Compound offers Chemical Resistance to Hydrocarbons & High Impact Strength from the Carbon Fiber

STAT-KON™ RE008 Nylon 6/6 Featured such as : -
- Electrically Conductive
- Excellent Strength
- High Heat Tolerance
- Good Abrasion and Wear Resistance
- Chemical Resistance to Hydrocarbons
- High Stiffness
- Wear Resistance and Lubricity

Applications Examples

- Electronic Components
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ RE008 Resin has a Flexural Modulus of 25000 MPa. 2 mm/min ISO 178

STAT-KON™ RE008 Resin offers a Tensile Strain, Break, 5 mm/min of 1.3%. ASTM D638

SABIC LNP™ STAT-KON™ RE008 compound offer HDT, 1.82 MPa of 256°C

LNP™ STAT-KON™ RE008 Compound Resin has -% Shrinkage, Along Flow

STAT-KON® RE008 Compound are UL94 - HB @ 1.5 mm