STAT-KON REL33 Compound. Nylon 6/6 with 15% Carbon Fiber & 15% PTFE

Polyamide 6/6 (PA6/6) Based. Wear resistant & Electrically Conductive

LNP™ STAT-KON™ REL33 Compound is a Nylon 6/10 with 15% Carbon Fiber & 15% PTFE Reinforced. Electrically Conductive with High Wear resistant and High Stiffness

the Compound Surface Resistivity = 1.E+01 - 1.E+04 Ω. Non UL Rated

the Polyamide 6/6 (PA6/6) Compound offers Chemical Resistance to Hydrocarbons & High Impact Strength from the Carbon Fiber

STAT-KON™ REL33 Nylon 6/6 featured such as : -
- Electrically Conductive
- excellent Strength
- High Heat Tolerance
- Good Abrasion and Wear Resistance
- Chemical Resistance to Hydrocarbons
- High Stiffness
- Higher Wear Resistance and Lubricity

applications Examples

- Electronic components
- material Handling

LNP™ STAT-KON™ offers Cost effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ REL33 Resin has a Flexural Modulus of 8580 MPa. 2 mm/min ISO 178

STAT-KON™ REL33 Resin offers a Tensile Strain, Break, 5 mm/min of 2.4%. ISO 527

SABIC LNP™ STAT-KON™ REL33 compound offer HDT, 1.82 MPa of 253°C

LNP™ STAT-KON™ REL33 Compound Resin has 0.3 ~ 0.6% Shrinkage, Along flow

STAT-KON® REL33 Compound are Non UL94 Listed