STAT-KON WX06322 Compound. PBT Resin with Carbon Fiber & Glass Fiber

Electrically Conductive, High Stiffness, Flame Retardant & High Heat

LNP™ STAT-KON™ WX06322 Compound is a Polybutylene Terephthalate Resin with Carbon Fiber & Glass Fiber Reinforced

The Compound Surface Resistivity = 1.30E + 06 Ω. UL94 Rated

STAT-KON™ WX06322 Featured such as : -
- Electrically Conductive
- Low Warpage
- High Stiffness
- High Strength
- Super Strong (Carbon Fiber Reinforced)
- High Heat Resistance

STAT-KON™ WX06322 offers Light Weight Structural Design for Critical Parts

Applications Examples

- Electronic Components
- Computer Tablets
- Electrical
- Material Handling

LNP™ STAT-KON™ offers Cost Effective Solutions for Parts avoiding Static Electricity Buildup or Discharge

STAT-KON™ WX06322 Resin has a Flexural Modulus of 11450 MPa. 2 mm/min ASTM D790

STAT-KON™ WX06322 Resin offers a Tensile Strain, Break, 5 mm/min of -%. ISO 527

SABIC LNP™ STAT-KON™ WX06322 compound offer HDT, 1.82 MPa of 204°C

LNP™ STAT-KON™ WX06322 Compound Resin has 0.17% Shrinkage, Along Flow

STAT-KON® WX06322 Compound are UL94 - HB @ 2.0 mm ~ 3.0 mm

STAT-KON Main Page