POLYLAC PA-709P is a General Extrusion ABS Resin for Pipes Extrusion

Good Finish and Best Flow Rate Grade offering Ease of Processing

POLYLAC™ PA-709P is a Extrusion Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The Advanced POLYLAC™ PA-709P Resin is a Cost Effectives Raw Materials resulting in Good Energy Consumption, Lower Equipment Maintenance while Achieving Cost-Effectiveness in the Pipes Extrusion.

POLYLAC™ PA-709P has Melt Flow Index of 5 ml/10 min ( Based on ISO 1133 Test Method ). It offers the Right Properties, such as Viscosity, Melt Flow Rate, and Temperature Resistance, to ensure Smooth Pipes Extrusion

POLYLAC™ PA-709P Featured such as : -
- Good Gloss
- Good Rigidity
- Good Impact Strength


CHIMEI POLYLAC™ PA-709P Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-709P Resin has a Flexural Modulus of 2 GPa. 2 mm/min ISO 178

POLYLAC™ PA-709P Resin offers a Tensile Elongation 50 mm/min of 40%. ISO 527

CHIMEI POLYLAC™ PA-709P compound offer HDT,75/A, 1.82 MPa Unannealed of -°C

CHIMEI POLYLAC™ PA-709P offer 39 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-709P ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm