POLYLAC PA-709S is a General Extrusion ABS Resin. Ultra High Impact

Good Gloss Finish and Flow Rate Grade for Ease of Processing

POLYLAC™ PA-709S is a Extrusion Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The Advanced Ultra High Impact of POLYLAC™ PA-709S Resin makes it a Popular Choice for Extrusion Parts where Stiffness is Critical. Widely Use in Piping Extrusion and featuring Ease of Processing when Extruded

POLYLAC™ PA-709S has Melt Flow Index of 4 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-709S Featured such as : -
- Good Gloss
- Good Rigidity
- Ultra High Impact Strength

CHIMEI POLYLAC™ PA-709S Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-709S Resin has a Flexural Modulus of 1.5 GPa. 2 mm/min ISO 178

POLYLAC™ PA-709S Resin offers a Tensile Elongation 50 mm/min of 50%. ISO 527

CHIMEI POLYLAC™ PA-709S compound offer HDT,75/A, 1.82 MPa Unannealed of 81°C

CHIMEI POLYLAC™ PA-709S offer 42 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-709S ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm