top of page

POLYLAC PA-726M is an ABS Resin Dedicated for Ease of Electroplating

Unique Features that Ensure Uniformly and Good Metal Coatiing Adhesion

POLYLAC™ PA-726M is a Electroplating Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The Unique POLYLAC™ PA-726M Resin offers Ease of Metal Coating Adhesion and Uniform Bonding of Electroplating. Therefore, the Finishing will Rresult in a High Quality, Durable Finish that meets the Desired Specifications for the Application such as Automotive Parts

POLYLAC™ PA-726M has Melt Flow Index of 23 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-726M Featured such as : -
- Good Finishing
- Good Rigidity
- Good Impact Strength
- Ease of Electroplating

CHIMEI POLYLAC™ PA-726M Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-726M Resin has a Flexural Modulus of 2.1 GPa. 2 mm/min ISO 178

POLYLAC™ PA-726M Resin offers a Tensile Elongation 50 mm/min of 70%. ISO 527

CHIMEI POLYLAC™ PA-726M compound offer HDT,75/A, 1.82 MPa Unannealed of 81°C

CHIMEI POLYLAC™ PA-726M offer 22 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-726M ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm