POLYLAC PA-747F is a Unique High Rigidity Profile Extrusion ABS Resin

Features Dimensional Stability, Processing and Good Melt Strength

POLYLAC™ PA-747F is a Extrusion Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The High Impact of POLYLAC™ PA-747F Resin makes it a Good Choice for Extrusion Parts where Good Melt Flow, Rigidity and Dimension Stability is Require.

POLYLAC™ PA-747F has Melt Flow Index of 3.5 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-747F Featured such as : -
- Good Gloss
- High Rigidity
- Good Impact Strength

CHIMEI POLYLAC™ PA-747F Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-747F Resin has a Flexural Modulus of 1.9 GPa. 2 mm/min ISO 178

POLYLAC™ PA-747F Resin offers a Tensile Elongation 50 mm/min of 35%. ISO 527

CHIMEI POLYLAC™ PA-747F compound offer HDT,75/A, 1.82 MPa Unannealed of 84°C

CHIMEI POLYLAC™ PA-747F offer 32 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-747F ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm