POLYLAC PA-747R is a Unique High Impact Profile Extrusion ABS Resin

Features Good Melt Strength with Dimensional Stability & Processing

POLYLAC™ PA-747R is a Extrusion Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The High Impact of POLYLAC™ PA-747R Resin makes it a Good Choice for Extrusion Parts where Good Melt Flow, Impact and Dimension Stability is Require.

POLYLAC™ PA-747R has Melt Flow Index of 2.5 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-747R Featured such as : -
- Good Gloss
- Good Rigidity
- High Impact Strength

CHIMEI POLYLAC™ PA-747R Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-747R Resin has a Flexural Modulus of 1.7 GPa. 2 mm/min ISO 178

POLYLAC™ PA-747R Resin offers a Tensile Elongation 50 mm/min of 40%. ISO 527

CHIMEI POLYLAC™ PA-747R compound offer HDT,75/A, 1.82 MPa Unannealed of 83°C

CHIMEI POLYLAC™ PA-747R offer 39 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-747R ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm