POLYLAC PA-756 is an ABS Grade with High Flow & Unique High Rigidity

Unique High Gloss Finishing with Ease of Processing & UL94-HB Rating

POLYLAC™ PA-756 is a High Flow Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The Unique High Flow POLYLAC™ PA-756 Resin makes it a Popular Choice Large Parts or Thin Wall Design. Added with High Rigidity & Superb High Gloss Finishing, this Grade is one of It's Kind in the Series

POLYLAC™ PA-756 has Melt Flow Index of 42 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-756 Featured such as : -
- High Gloss
- High Rigidity
- Great High Flow

CHIMEI POLYLAC™ PA-756 Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-756 Resin has a Flexural Modulus of 2.1 GPa. 2 mm/min ISO 178

POLYLAC™ PA-756 Resin offers a Tensile Elongation 50 mm/min of 75%. ISO 527

CHIMEI POLYLAC™ PA-756 compound offer HDT,75/A, 1.82 MPa Unannealed of 83°C

CHIMEI POLYLAC™ PA-756 offer 15 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-756 ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm