POLYLAC PA-756H is a Ultra Flow Thin Wall ABS Resin for Large Parts

General Impact Strength with Ease of Processing & UL94-HB Rating

POLYLAC™ PA-756H is a High Flow Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties.

The Unique High Flow POLYLAC™ PA-756H Resin makes it a Popular Choice Large Parts or Thin Wall Design. It Has a Insanely High Melt Flow Rate, which means it can be Easily Molded into Complex Shapes and Structures.

POLYLAC™ PA-756H has Superb Melt Flow Index of 80 ml/10 min ( Based on ISO 1133 Test Method ). In Addition to it's Superb High Flow, Fair Impact Resistance.

Examples of application for this Resin will be Automotive Parts ( Interior Trim, or Exterior Body Panels), Electronics ( Computer Housings, or Printer Body), Toys, Due to its Durability and Ability to be Molded into Various Shapes and Appliances ( Rrefrigerator Body Parts, Washing Mmachine Components, and Vacuum Cleaner Housings)

POLYLAC™ PA-756H Featured such as : -
- Good Gloss
- Good Rigidity
- Fair Impact Strength

CHIMEI POLYLAC™ PA-756H Compound Resin has 0.4 ~ 0.7% Mold Shrinkage

POLYLAC™ PA-756H Resin has a Flexural Modulus of 2.2 GPa. 2 mm/min ISO 178

POLYLAC™ PA-756H Resin offers a Tensile Elongation 50 mm/min of 50%. ISO 527

CHIMEI POLYLAC™ PA-756H compound offer HDT,75/A, 1.82 MPa Unannealed of 82°C

CHIMEI POLYLAC™ PA-756H offer 9 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-756H ABS Resin are UL94 - HB@1.5 mm ~ 3.0 mm