POLYLAC PA-764G is an ABS Resin, Improved Flame Retardant Opaque Grade

Improved Flow Ability with High Heat Resistance & UL94-V0@1.0 mm

POLYLAC™ PA-764B is a FR Grade ABS Resin Developed by CHIMEI, Taiwan. The Acrylonitrile Butadiene Styrene, is a Thermoplastic Polymer that is commonly used in a Wide Range of Applications due to its Strong and Durable Properties. Good Flow

The Good Weather Ability, Improved Flame Retardant Series of POLYLAC™ PA-764B Opaque Colored, High Heat Resistance. Flame retardants are added to Reduce their Flammability and Slow Down or Prevent the Spread of Fire for High Power Electrical Parts. UL94 2.5mm ~ 2.8 mm 5VA

POLYLAC™ PA-764B ABS Resin has Melt Flow Index of 29 ml/10 min ( Based on ISO 1133 Test Method )

POLYLAC™ PA-764B Featured such as : -
- Good Weather Ability
- Opaque Colored
- High Impact Strength
- Better Flame Retardant
- High Heat Resistance

CHIMEI POLYLAC™ PA-764G Compound Resin has 0.3 ~ 0.6% Mold Shrinkage

POLYLAC™ PA-764G Resin has a Flexural Modulus of 1.8 GPa. 2 mm/min ISO 178

POLYLAC™ PA-764G Resin offers a Tensile Elongation 50 mm/min of 10%. ISO 527

CHIMEI POLYLAC™ PA-764G compound offer HDT,75/A, 1.82 MPa Unannealed of 82°C

CHIMEI POLYLAC™ PA-764G offer 12 KJ/m2 at 23°C Notched Charp Impact Strength

CHIMEI POLYLAC™ PA-764G ABS Resin are UL94 - V0@1.0 mm ~ 2.8 mm