VALOX™ 553 PBT/PC 30% Glass Reinforced Resin. Good Flame Retardant
Excellent Chemical Resistance, Low Warpage & Low Shrinkage Properties
VALOX™ 553 PBT/PC Resin features 30% Glass Reinforcement, delivering High Stiffness and Strong structural support. The Advance Resin provides Stable Mechanical Performance under Load, helping reduce deformation during service. This Reinforced Blend supports Durable Parts in Enclosures, Frames, and Structural Hardware applications Reliability
Flame Retardant Performance is a Key Benefit of VALOX™ 553 PBT/PC Resin, supporting safer Designs in Regulated Markets. It achieves UL94 V-0 Rating at 0.80 mm to 3.00 mm Thickness, thus meeting Fire Safety requirements. This Capability makes VALOX™ 553 PBT/PC Resin suitable for Electrical Housings and Power Related Components Compliance
Low Warpage Performance Helps VALOX™ 553 PBT/PC Resin maintain Flatness in Larger Molded Parts. Low Shrinkage Characteristics help it deliver better Dimensional Control after Cooling, supporting Tight Tolerances. These processing advantages improve Part Consistency, Reduce Rework Risk, and support Higher Yield in Manufacturing Operations Efficiency
VALOX™ 553 delivers excellent Chemical Resistance, supporting Long Service Life in Automotive, Electrical, and Industrial Environments. VALOX™ 553 PBT/PC Resin is a ROHS Compliant Grade, supporting Environmental requirements and Global Regulatory acceptance. This combination of reinforcement, Flame Retardancy, Low Warpage, and Chemical Durability makes VALOX™ 553 PBT/PC Resin a Right Choice for High Performance applications Markets
Notes:
VALOX™ 553 PBT/PC Resin
30% Glass Reinforced
Impact Modified
UL94 Rated
ROHS Compliant Grade
VALOX 553 PBT/PC has 0.5 Shrinkage, Flow, 3.2 mm. %
Material HDT, 1.82 MPa, ASTM A648, °C
3.2 mm, unannealed 138
Vicat Softening Temperature Rate
Vicat Softening Temperature rate , B120 = 161
Material MFI / Melt Flow Rate
Melt Flow Rate, 266°C/5.0 kgf = 40
Material Melt Volume Rate, MVR
Melt Volume Rate, 265°C/5.0 kgf = 30
VALOX™ 553 Resin has a Flexural Modulus of 9500 MPa. 2 mm/min ISO 178
VALOX™ 553 Resin are UL94 - V-0, 0.80 mm ~ 3.00 mm Rated
Disclaimer
Any sale by SABIC, Its Subsidiaries and Affiliates (each a “Seller”), is Made Exclusively under Seller’s Standard Conditions of Sale (available upon request) unless Agreed Otherwise in Writing and Signed on behalf of the Seller. While the Information Contained herein is given in Good Faith, SELLER MAKES NO WARRANTY, EXPRESS OR IMPLIED, INCLUDING MERCHANTABILITY AND NONINFRINGEMENT OF INTELLECTUAL PROPERTY, NOR ASSUMES ANY LIABILITY, DIRECT OR INDIRECT, WITH RESPECT TO THE PERFORMANCE, SUITABILITY OR FITNESS FOR INTENDED USE OR PURPOSE OF THESE PRODUCTS IN ANY APPLICATION. Each Customer must Determine the Suitability of Seller Materials for the Customer’s Particular Use through Appropriate Testing and Analysis. No Statement by Seller Concerning a Possible Use of any Product, Service or Design is Intended, or should be Construed, to grant any License under any Patent or other Intellectual Property Right. © 2021